ABSTRACT Purpose: To study the influence of silver nanoparticles (AgNP) on tissue reaction when incorporated into a polymeric matrix of polyacrylic acid-based (Carbopol®) gel as a proposal for a new low-cost type of biomaterial that is simple to manufacture for use as an antimicrobial and antioxidative dressing. Methods: In-vivo tests of implantation in the subcutaneous tissue of the back of rats were performed using polyethylene tubes in three situations: empty, only the gel, and gel incorporated with AgNP. Then, the tissue reaction was studied by counting inflammatory cells. Additionally, in-vitro tests of the antioxidative and antimicrobial activity of AgNP were performed. The radical 2,2 diphenyl-1 picrylhydrazyl (DPPH) was used to test the antioxidative activity of AgNP using electron spin resonance. The antimicrobial activity of AgNP was determined by minimum inhibitory concentration against the microorganisms: Staphylococcus aureus, Pseudomonas aeruginosa, and Escherichia coli. Results: The results indicated that AgNP presents antioxidative activity and was able to inhibit the growth of the microorganisms tested. The addition of AgNP in Carbopol® did not alter the tissue inflammatory response (p>0.05, Kruskal-Wallis’s test). Conclusions: The new biomaterial is promising for future use as a dressing for its beneficial properties for regenerative processes.

Abstract In this work, the natural latex extracted from Harconia speciosa was incorporated with silver nanoparticles (AgNP) to compose a functional biomaterial associating the intrinsic angiogenic activity of the latex and the antimicrobial activity of AgNP. Tissue reaction after subcutaneous implantation in dorsum of rats of membranes without AgNP and with 0.05%, 0.4% AgNP was compared at 3, 7 and 25 days. No statistically significant difference in the tissue response of the different biomaterials was observed, indicating that AgNP did not interfere with the inflammatory reaction (p > 0.05) or with the angiogenic activity of latex. Biomembranes were also tested against bacterial biofilm formation by Staphylococcus aureus and the antimicrobial activity of the new biomaterial can be found with bacteria crenation (0.05% AgNP) and no biofilm deposition (0.4% AgNP). Therefore, this biomaterial has interesting properties for the tissue repair process and may be feasible for future applications as dressing.